Ffactorau sy'n effeithio ar rym angori pigau a dulliau ar gyfer eu gwella
- Beth yw'r ffactorau craidd sy'n effeithio ar rym angori pigyn?
The strength of anchoring materials is crucial. The compressive strength of sulfur anchoring agent must be ≥40MPa; if it is lower than 30MPa, the anchoring force will decrease by 30% - 40%. The water - cement ratio must be controlled within the range of 0.3 - 0.35. The fit gap between the nail hole diameter and the spike should be moderate. An excessively large gap (>Bydd 3mm) yn lleihau'r grym angori 20% - 25%, tra bod bwlch rhy fach (<1mm) makes it difficult for the anchoring agent to fill. The optimal gap is 1.5 - 2mm to ensure uniform wrapping force. Insufficient spike embedding depth (<100mm) will reduce the anchoring force by 40% - 50%. The standard embedding depth should be 120 - 150mm, and the embedded part must have threads or barbs to increase mechanical biting force. Insufficient pouring of anchoring agent (voids >Bydd 5%) yn achosi crynodiad straen lleol, ac mae'r amrywiad grym angori yn cyrraedd 15%- 20%. Rhaid defnyddio tywallt pwysau i sicrhau crynoder.
- Beth yw'r gwahaniaethau mewn grym angori pigyn ymhlith gwahanol ddeunyddiau angori?
Sulfur anchoring agent (sulfur: cement: sand {{0}}:0.3:1.5) has an anchoring force of 60 - 80kN, with fast setting (30 minutes), but it is easy to embrittle at low temperatures (anchoring force decreases by 20% at - 20 degree ), widely used in ordinary railways. Mae gan asiant angori resin (asiant halltu epocsi + halltu) rym angori o 80 - 100 kN, gyda gwrthiant tywydd da. Mae'r newid grym angori yn llai na neu'n hafal i 10% yn yr ystod o radd - 40 - 60, ond mae ei gost yn 50% - 60% yn uwch nag asiant angori sylffwr, a ffefrir ar gyfer rheilffyrdd cyflym a rhanbarthau oer. Mae gan asiant angori morter sment rym angori is (40 - 60 kn) ond diogelu'r amgylchedd da, sy'n addas ar gyfer cludo rheilffyrdd trefol. Rhaid ychwanegu 5% - 8% 膨胀剂 i wneud iawn am grebachu ac osgoi angori gwanhau grym. Mae gan asiant angori cyfansawdd (resin + ffibr dur) rym angori o 100 - 120 kn. Pan fydd y cynnwys ffibr dur yn 3% - 5%, mae'r cryfder cneifio yn cynyddu 25% - 30%, a ddefnyddir mewn rhannau allweddol o reilffyrdd trwm - cludo.
- Sut mae'r broses adeiladu yn effeithio ar rym angori pigyn?
Incomplete cleaning of nail holes (residual dust >Bydd 5%) yn lleihau'r grym angori 15%- 20%. Rhaid defnyddio gynnau aer pwysau uchel ar gyfer glanhau, a rhaid defnyddio brwsys gwifren os oes angen i sicrhau dim slag arnofio ar wal fewnol tyllau ewinedd. Tymheredd arllwys rhy isel asiant angori (<130℃ for sulfur anchoring) will lead to poor fluidity and incomplete filling, reducing the anchoring force by 25% - 30%. The pouring temperature must be controlled at 140 - 160℃. A deviation of spike insertion depth >Bydd 5mm yn gwneud y dosbarthiad grym angori yn anwastad, a gall gwahaniaeth grym angori pigau yn yr un swp gyrraedd 10% - 15%. Rhaid defnyddio offer lleoli wrth eu mewnosod i sicrhau dyfnder unffurf, gyda gwyriad yn llai na neu'n hafal i 3mm. Amser halltu annigonol (<24 hours) will make the anchoring agent strength not up to standard, and the anchoring force is only 70% - 80% of the design value. Resin anchoring agent needs to be cured for more than 48 hours, and sulfur anchoring agent needs to be naturally cooled to room temperature (≥6 hours).
- Sut mae ffactorau amgylcheddol yn effeithio ar rym angori pigyn?
A humid environment will reduce the bonding force between the anchoring agent and the nail hole. When the relative humidity is >90%, the anchoring force decreases by 10% - 15%. Rainy day construction must take rainproof measures to ensure that the nail hole is dry (moisture content ≤5%). A high - temperature environment (≥35℃) will accelerate the curing of resin anchoring agent, and concentrated reaction heat release may cause internal cracking, with an anchoring force loss of 20% - 25%. Retarders must be added to the anchoring agent to extend the gel time to 30 - 40 minutes. Freeze - thaw cycles (- 20 - 20℃) will cause microcracks in the anchoring agent. After 200 cycles, the anchoring force decreases by 30% - 40%. Frost - resistant anchoring agent (adding air - entraining agent, air content 3% - 5%) must be selected in cold regions. Saline - alkaline soil will erode the anchoring agent. When the chloride ion concentration is >500mg/L, mae'r grym angori yn gwanhau 5% - 8% bob blwyddyn. Rhaid defnyddio pigau wedi'u gorchuddio â gwrth -gyrydiad ac asiant angori gwrthsefyll alcali mewn ardaloedd arfordirol.
- Beth yw'r mesurau penodol i wella grym angori pigyn?
Optimeiddio'r fformiwla asiant angori: gall ychwanegu 5% - 8% powdr graffit at asiant angori sylffwr gynyddu'r grym angori 10% - 15% a gwella hylifedd; Mae ychwanegu 1% - 2% asiant cyplu silane i asiant angori resin yn gwella'r grym bondio rhyngwyneb â phigau. Mabwysiadu cymorth angori mecanyddol: rholio llinellau oblique (traw 3 - 4 mm) ar wyneb y pigyn i gynyddu grym brathu mecanyddol gyda'r asiant angori, gan gynyddu'r grym angori 20% - 25%. Rhaid i bigau rheilffordd trwm - Haul fabwysiadu'r strwythur hwn. Gwella'r broses adeiladu: cyn -gynhesu'r twll ewinedd (gradd 40 - 50) i wella hylifedd yr asiant angori, gan gynyddu'r crynoder llenwi 15% - 20%, yn arbennig o addas ar gyfer adeiladu gaeaf. Canfod y grym angori yn rheolaidd: mae 10% o bigau mewn rheilffyrdd cyffredin yn cael eu samplu bob 2 flynedd. Mae angen ail -angori'r rhai sydd â grym angori sy'n is nag 80% o'r gwerth dylunio. Mae rheilffyrdd cyflym yn cael eu canfod unwaith y flwyddyn i sicrhau bod y grym angori yn cwrdd â'r safon (sy'n fwy na neu'n hafal i 60kN).